The objective of this study was to evaluate fracture strength of high-translucent (HTZ) and low-translucent (LTZ) zirconia and glass-ceramic (LDS) crowns. HTZ and LTZ crowns were made with thicknesses of; 0.3 mm, 0.5 mm, 0.7 mm, 1.0 mm, and 1.5 mm; and LDS crowns of 1.0 mm and 1.5 mm thicknesses. Each group consisted of 10 crowns. All crowns underwent artificial aging before loading until fracture. Mean fracture strengths varied from 450 N to 3,248 N in the LTZ group, 438 N to 3,487 N in the HTZ group, and 1,030 N to 1,431 N in the LDS group. The load at fracture of HTZ and LTZ crowns was equal. The load at fracture of yttria-stabilized tetragonal zirconia polycrystals crowns was significantly greater than LDS crowns (P = 0.000). Two types of fractures were recorded; complete and partial crack-like fracture. The crack type fracture occurred most frequently in all groups except in the thicker LTZ groups (1.0 mm and 1.5 mm). According to this study, there is no difference in strength between crowns made of high-translucent or low-translucent zirconia. At equal thickness, the strength of zirconia crowns was significantly greater than that of lithium-disilicate glass-ceramic.